DILLE, J ; Areiza, M.C.L. ; TAVARES, S.S.M. ; Pereira, G.R. ; DE ALMEIDA, L.H. ; Rebello, J.M.A. .
Resumo: Duplex stainless steels are high strength and corrosion resistant alloys extensively used in chemical and petrochemical industries. However, exposition to temperatures in the range 300–1000 °C leads to precipitation of different phases having a detrimental effect on the mechanical properties and on the corrosion resistance of the alloy. In this work, the microstructural evolution during aging of a UNS S32304 lean duplex stainless steel was investigated by scanning electron microscopy, transmission electron microscopy and magnetic force microscopy. Formation of secondary austenite as well as Cr2N and Cr23C6 precipitation and, consequently, a decrease of ferrite volume fraction were observed. EDX analysis indicated that secondary austenite is depleted in chromium which is detrimental to the corrosion resistance of the alloy. A variation of magnetic properties and Eddy current measurement parameters during aging was simultaneously detected and can be explained by the decrease of ferrite volume content. Therefore, Eddy current non-destructive testing can be successfully applied to detect the formation of deleterious phases during aging.